Dr. WANG Rong’s research team at the Cixi Institute of Biomedical Engineering, Ningbo Institute of Materials Technology and Engineering (NIMTE), Chinese Academy of Sciences (CAS), has recently developed a mechano-responsive antibacterial hydrogel with controllable drug release behavior for wound healing application, in cooperation with researchers at Sun Yat-sen University (SYSU) and Nanchang University (NCU). The study was published in ACS Applied Materials & Interfaces.
In recent decades, hydrogels for wound healing have attracted tremendous attention around the globe. However, acute cutaneous wounds on moving body parts usually suffered from various mechanical forces, such as stretching forces and compressive forces under dynamic circumstances, thus the healing process was easily interfered. However, traditional hydrogels have limited efficacy owing to their poor mechanical properties, skin adhesiveness and drug delivery efficiency.
To address this problem, a tough, antibacterial, drug-loaded mechano-responsive zwitterionic hydrogel was designed. Diacrylate Pluronic F127 (F127DA) micelles were used as macro-cross-linkers and drug carriers.The developed micelle-cross-linked hydrogel showed superior mechanical properties, with the ultimate tensile strength and tensile strain of up to 112 kPa and 1420%, respectively, and compressive stress of up to 1.41 MPa.
Besides, poly(sulfobetaine methacrylate) (polySBMA) endowed the hydrogel with excellent tissue adhesiveness (～6 kPa) and antifouling property. When the micelle-crosslinked hydrogel was subjected to mechanical forces, the weak hydrophobic association in the micelles was destroyed, the combination between bioactive drug and the micelle core was destabilized, resulting in responsive drug release behavior. Results showed that the drug release from the hydrogel could be precisely controlled by mechanical strength and cycles, which endowing the hydrogel a broad-spectrum antibacterial property against both Gram-positive and Gram-negative bacteria.
In addition, zwitterionic polySBMA possesses high hydration ability to form a stable repulsive boundary layer under aqueous conditions, thus the prepared hydrogel effectively inhibited protein adsorption and bacteria adhesion. Furthermore, the hydrogel showed good biocompatibility to mammal cells and efficiently promoted wound healing in a full-thickness skin defect mice model.
This tough, mechano-responsive, antibacterial and biocompatible hydrogel holds great promise for wound treatment in a complex dynamic environment.
The work was supported by the National Natural Science Foundation of China (No. 51803229, 51873224, and 52011530019), National Key Research and Development Program of China (No. 2018YFE0119400), S&T Innovation 2025 Major Special Program of Ningbo (No. 2018B10040), and Natural Science Foundation of Zhejiang Province (No. LQ19E030006).
Fig. Schematic illustration of mechano-responsive hydrogel for wound healing (Image by NIMTE)